SAE1006 High speed controlled cold and hot rolling wire delivery status: hot rolling controlled cold standard :Q/ASD18-2004

Chemical composition:

C-0.06P-0.008S-0.004 Cr-0.0200 Si-0.04 Mn-0.31 Ni-0.0100

Cu - 0.0040 -

Performance test:

Yield strength :270Mpa

Tensile strength :380Mpa

Elongation :33.5%

SAE1006 Features:

It has the characteristics of high elongation, smooth surface to achieve mirror effect, thickness standard, flat shape, rust resistance, etc., suitable for all kinds of metal stamping, good tensile performance. Such as LED bracket, rotor, lighting, fan, motorcycle fuel tank, steel pipe, household appliances and shell and other hardware products. Adopting SAE1006, the production facilities are equipped with hot-rolled plate surface treatment pickling line, bright hood annealing furnace, four-bar reversible cold rolling, and equipped with plate surface precision levelling unit, stress relief plane tension straightening machine, high precision strip unit

------------------------------------------------------------------------------------------------------------------------------

SAE1008 High speed controlled cold and hot rolling rod delivery status: hot rolling controlled cold

Standard :Q/ASD18-2004

Chemical composition(%):

C-0.06Si-0.06Mn-0.38P-0.009S-0.006Cr-0.0100 Ni-0.0100

Cu - 0.0010 -

Performance test:

Yield strength :295-302Mpa,

Tensile strength :394-403Mpa,

Elongation :30-30.5%

This kind of steel has a large output and a wide range of uses, and is generally made of round, square, flat and other profiles, plates and seamless steel pipes by multi-rolling (forging). It is mainly used in the manufacture of general structures and mechanical structures, components, building structures and pipelines for conveying fluids.

------------------------------------------------------------------------------------------------------------------------------

SAE1010Chemical composition(%):

C ：0.08～0.13， Si：0.15～0.35， Mn：0.30～0.60， S ：≤0.050， P ：≤0.040， Cr：≤0.20， Ni：≤0.25， Cu：≤0.25

1010 steel is a high-quality carbon structural steel, low mechanical strength, plasticity, toughness, cold state easy to die forming, easy to cut processing, good welding performance, in order to improve the surface hardness can be carburized and cyanide treatment. For the manufacture of low strength welding parts, cold stamping parts, forgings and carburized parts such as bolts, washers, partitions, shells, etc.